Hunt, Christopher Paul. (1987) Influence of residual elements on the intergranular stress corrosion cracking of carbon manganese steel. Doctoral thesis, University of Surrey (United Kingdom)..

Available under License Creative Commons Attribution Non-commercial Share Alike.

Download (8MB) | Preview


The Influences of five common tramp elements P, S, Sn, Cu, and Ni at typical residual levels on the intergranular stress corrosion cracking (IGSCC) of a typical mild steel. (0.15%C, 0.8%Mn and 0.05%Si), are studied in nitrate solutions and a mixture of carbonate and bicarbonate solutions. The relative effects of these impurities are examined in terms, of the electrochemical properties of unstressed material, of the IGSCC susceptibility in a constant strain rate test, and of the grain boundary and surface oxide compositions via surface analysis. Results show that in general only phosphorus can be detrimental. A slight beneficial effect is apparent for Cu in both electrolytes. Phosphorus has small adverse effects in certain narrow potential regions in the NH[4]NO[3] electrolyte. These occur just above the free corrosion potential and above the active-passive transition (1100 mV). There are no detrimental effects due to the impurities in the carbonate/bicarbonate electrolyte. The negligible effects of impurities occurs in spite of impurity concentrations at the grain boundaries being significantly enhanced above the bulk to 10%. as confirmed by Auger electron spectroscopy. Hence, the IGSCC susceptibility is shown to be dominated by the carbon present in the steel. XPS measurements indicate that carbon is present throughout the oxide, and importantly up to the electrolyte interface. IGSCC susceptibility is thought to occur principally by a breakdown in the oxide integrity, which leads to prolonged chemical attack. This mechanism is attibuted to the action of carbon and possibly the impurities, however under certain conditions some secondary mechanisms are needed to account for ail the effects due to the impurities. These include improved passivation by reaction products and a remedial influence on the detrimental effect of carbon.

Item Type: Thesis (Doctoral)
Divisions : Theses
Authors :
Hunt, Christopher Paul.
Date : 1987
Contributors :
Additional Information : Thesis (Ph.D.)--University of Surrey (United Kingdom), 1987.
Depositing User : EPrints Services
Date Deposited : 22 Jun 2018 13:02
Last Modified : 06 Nov 2018 16:52

Actions (login required)

View Item View Item


Downloads per month over past year

Information about this web site

© The University of Surrey, Guildford, Surrey, GU2 7XH, United Kingdom.
+44 (0)1483 300800