‘Inorganics-in-organics’ semiconductors for high energy radiation detection.

Thirimanne, Hashini (2019) ‘Inorganics-in-organics’ semiconductors for high energy radiation detection. Doctoral thesis, University of Surrey.

[img] Text (PhD Thesis)
Thesis_H Thirimanne.pdf - Version of Record
Restricted to Repository staff only until 31 January 2022.
Available under License Creative Commons Attribution Non-commercial Share Alike.

Download (9MB) | Request a copy
[img] Text (Embargo form)
Thesis embargo Hashini Thirimanne.pdf
Restricted to Repository staff only
Available under License Creative Commons Attribution Non-commercial Share Alike.

Download (93kB) | Request a copy


X-ray detectors are an invaluable tool for healthcare diagnostics, cancer therapy, homeland security and non-destructive evaluation among many fields. However, potential uses for X-rays are limited by system cost and/or detector dimensions. Current X-ray detector sensitivities are limited by the bulk X-ray attenuation of the materials and consequently necessitates thick crystals with dimensions of ~ 1 mm – 1 cm, resulting in rigid structure, high operational voltages and high cost. Semiconducting polymer X-ray detectors are an emerging low cost technology. Their solution processable nature enables the fabrication of such detectors on flexible substrates over large areas using printing and roll-to-roll coating techniques. However, the low atomic number (Z) of organic materials results in low X-ray attenuation and hence, low X-ray sensitivities. This thesis focuses on direct detection of X-rays using organic semiconducting systems incorporating high Z Bi2O3 nanoparticles (NPs). For the work discussed, a thick organic bulk heterojunction (~10 – 20 μm) consisting of the p-type poly(3-hexylthiophene-2,5-diyl) (P3HT) and the n type [6,6]-Phenyl C71 butyric acid methyl ester (PC70BM) are utilised. The effectiveness on the utilisation of a dual carrier system is demonstrated through the fabrication of detectors in a diode architecture by varying the NP loading from 0 – ~50% (by wt.). These hybrid detectors demonstrate sensitivities of 1712 μC mGy-1 cm-3 when irradiated under 50 kV tungsten X-ray source and ~30 and 58 μC mGy-1 cm-3 under 6 and 15 MV X-rays generated from a medical linear accelerator. A flexible detector was fabricated which demonstrated a high sensitivity approaching 300 μC mGy-1 cm-3, highlighting the promise of the technology for dosimetry and imaging in non-planar architectures. These performances are discussed based on the structural and electrical characteristics of the hybrid thick film diodes. Possible mechanisms for the high sensitivity observed are proposed where photoconducting gain, impact ionisation and Mie scattering are identified as central contributors towards the detector sensitivity. Routes to increasing the detector thickness to 100 μm – 1 mm thickness range is demonstrated using a pellet based on powder sintering technique. These P3HT:PC70BM:Bi2O3 detectors operate as photoconductors showing X-ray sensitivities in the region of ~ 160 C mGy-1 cm-3 and a preliminary X-ray imager based on the pellets are fabricated. Finally, potential routes for further improvement of the detector characteristics are discussed.

Item Type: Thesis (Doctoral)
Divisions : Theses
Authors :
Thirimanne, Hashini
Date : 31 January 2019
Funders : Leverhulme Trust
DOI : 10.15126/thesis.00850053
Grant Title : Leverhulme Trust
Contributors :
Uncontrolled Keywords : X-ray detector, nanomaterials, Direct detection
Depositing User : Hashini Thirimanne
Date Deposited : 07 Feb 2019 09:04
Last Modified : 07 Feb 2019 09:04

Actions (login required)

View Item View Item


Downloads per month over past year

Information about this web site

© The University of Surrey, Guildford, Surrey, GU2 7XH, United Kingdom.
+44 (0)1483 300800